preparationofcompositeadsorbentofsawdustandcacl2bycarbonizationmethodforcreatingpore
Bu Xianbiao; Wang Lingbao; Li Huashan; Lu Zhenneng
2012
Source Publicationsciencechinatechnologicalsciences
ISSN1674-7321
Volume055Issue:009Pages:2404
AbstractTo solve the problem of swelling and agglomeration of CaCl2 during the process of ammonia adsorption and improve the performance of mass transfer, we present a new method for the preparation of adsorbent. The CaCl2 is first immerged into sawdust by soaking method, then the composite adsorbent is prepared by carbonizing the mixture of CaCl2 and sawdust. The SEM image and elements analysis indicated that the new adsorbent has high porosity and uniform distribution of CaCl2 due to carbonization under temperature of 700℃. The performance testing of ammonia adsorption showed that under the conditions of evaporation temperature of -5℃ and condensation temperature of 40℃, the ammonia uptake reaches 0.204, 0.253 and 0.285 kg/kg, the specific cooling power (SCP) is 868.96, 540.02 and 405.16 W/kg, and the average adsorption rate is 6.79×10^-4, 4.22×10^-4 and 3.17×10^-4 kg/kg/s when the adsorption time is 5, 10 and 15 min, respectively. The problems of swelling and agglomeration of CaCl2 are solved.
Language英语
Document Type期刊论文
Identifierhttp://ir.giec.ac.cn/handle/344007/20026
Collection中国科学院广州能源研究所
Affiliation中国科学院广州能源研究所
First Author AffilicationGuangZhou Institute of Energy Conversion,Chinese Academy of Sciences
Recommended Citation
GB/T 7714
Bu Xianbiao,Wang Lingbao,Li Huashan,et al. preparationofcompositeadsorbentofsawdustandcacl2bycarbonizationmethodforcreatingpore[J]. sciencechinatechnologicalsciences,2012,055(009):2404.
APA Bu Xianbiao,Wang Lingbao,Li Huashan,&Lu Zhenneng.(2012).preparationofcompositeadsorbentofsawdustandcacl2bycarbonizationmethodforcreatingpore.sciencechinatechnologicalsciences,055(009),2404.
MLA Bu Xianbiao,et al."preparationofcompositeadsorbentofsawdustandcacl2bycarbonizationmethodforcreatingpore".sciencechinatechnologicalsciences 055.009(2012):2404.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Bu Xianbiao]'s Articles
[Wang Lingbao]'s Articles
[Li Huashan]'s Articles
Baidu academic
Similar articles in Baidu academic
[Bu Xianbiao]'s Articles
[Wang Lingbao]'s Articles
[Li Huashan]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Bu Xianbiao]'s Articles
[Wang Lingbao]'s Articles
[Li Huashan]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.