A ternary composite oxides S2O82-/ZrO2-TiO2SiO2 as an efficient solid super acid catalyst for depolymerization of lignin

GIEC OpenIR > 中国科学院广州能源研究所

	A ternary composite oxides S2O82-/ZrO2-TiO2SiO2 as an efficient solid super acid catalyst for depolymerization of lignin
	Wang, Huizhen ; Li, Wenzhi ; Wang, Jindong ; Chang, Hou-min ; Jameel, Hasan ; Zhang, Qi ; Li, Song ; Jin, Lele
	2017
发表期刊	RSC ADVANCES
卷号	7 页码:50027-50034
其他摘要	The solid, super, acid catalyst S2O82-/ZrO2-TiO2-SiO2, which has both a strong Bronsted acid and Lewis acid, was prepared and applied in lignin depolymerization. The results indicate that S2O82-/ZrO2-TiO2SiO2 is an effective catalyst for lignin depolymerisation since the liquid product was almost completely dissolved in ethyl acetate, indicating that it was comprised of mostly oligomeric lignin degradation products. The effect of hydrogenation co-catalysts (Pd/C, Pt/C and Ru/C, Rh/C) were also studied and found to improve the yield of aromatic compounds and the petroleum ether soluble fraction, which are mostly monomeric and dimeric products. The resulting yields of aromatic compounds and petroleum ether soluble products were 14.8% and 46%, respectively, when S2O82-/ZrO2-TiO2-SiO2 and Pt/C mixed catalyst was used at 310 degrees C for 24 hours. These results show that the use of a combination Bronsted and Lewis acid catalyst in combination with a hydrogenation catalyst (S2O82-/ZrO2-TiO2-SiO2 together with a noble metal catalyst) opens a practical route for efficient lignin depolymerization.
文献类型	期刊论文
条目标识符	http://ir.giec.ac.cn/handle/344007/16741
专题	中国科学院广州能源研究所
推荐引用方式 GB/T 7714	Wang, Huizhen,Li, Wenzhi,Wang, Jindong,et al. A ternary composite oxides S2O82-/ZrO2-TiO2SiO2 as an efficient solid super acid catalyst for depolymerization of lignin[J]. RSC ADVANCES,2017,7:50027-50034.
APA	Wang, Huizhen.,Li, Wenzhi.,Wang, Jindong.,Chang, Hou-min.,Jameel, Hasan.,...&Jin, Lele.(2017).A ternary composite oxides S2O82-/ZrO2-TiO2SiO2 as an efficient solid super acid catalyst for depolymerization of lignin.RSC ADVANCES,7,50027-50034.
MLA	Wang, Huizhen,et al."A ternary composite oxides S2O82-/ZrO2-TiO2SiO2 as an efficient solid super acid catalyst for depolymerization of lignin".RSC ADVANCES 7(2017):50027-50034.