外加剂对建筑垃圾再生砖早强性能的影响
Alternative TitleEffects of Additives on the Early Strength Performance of Construction Waste Regeneration Brick
鲁敏1,2,3; 熊祖鸿1,2,3; 林霞1,2,3; 房科靖1,2,3; 郭华芳1,2,3; 陈勇1,2,3
2017-12
Source Publication新能源进展
ISSN2095-560X
Volume5Issue:6Pages:466-471
Abstract选用两种减水剂和四种早强剂对建筑垃圾再生砖进行改性,研究了其掺量对建筑垃圾再生砖早期抗压强度(8h)的影响,并对不同龄期的建筑垃圾再生砖进行了XRD表征.实验结果显示:适量减水剂的添加可促进水化反应的进行,并抑制钙矾石晶核的过快生长,当聚羧酸系减水剂掺量为0.3%时,相应再生砖早期抗压强度可达10.45MPa.早强剂NaCl、Na2SiO3·9H2O和Na2CO3可降低水化反应过程中Ca2+的浓度,减缓钙矾石晶核的生长速度,其中NaCl添加量为2%时,再生砖早期抗压强度可增加20%以上.而添加三乙醇胺(TEOA)的早龄期建筑垃圾再生砖中水化硅酸钙的XRD峰强度较低,后期强度则较高,说明水化硅酸钙的形成具有一定迟滞性.
Other AbstractTwo kinds of superplasticizers and four kinds of hardening accelerators were selected to modify the construction waste regeneration brick. Effect of additive amount on the early compressive strength (8 h) of the construction waste regeneration brick was studied, and the characteristics of construction waste regeneration brick at different ages were characterized by XRD. Results showed that the hydration reaction was promoted by an appropriate amount of superplasticizer, and the growth of ettringite crystal nucleus was slowed down. The early compressive strength of regeneration brick reached 10.45 MPa when the addition amount of polycarboxylate superplasticizer was 0.3%. Hardening accelerators such as NaCl, Na2SiO3·9H2O and Na2CO3 can reduce the Ca2+ concentration during hydration reaction process, and inhibit the growth of ettringite crystal nucleus. The early compressive strength of the brick increased by more than 20% when the addition amount of NaCl was 2%. While adding triethanolamine (TEOA), the XRD peak strength of calcium silicate hydrate in early age construction waste regeneration brick was low, and then increased significantly with the brick age increase, indicating that the formation of calcium silicate hydrates was with certain hysteresis.
Keyword建筑垃圾再生砖 减水剂 早强剂 钙矾石 construction waste regeneration brick superplasticizer hardening accelerator ettringite
DOI10.3969/j.issn.2095-560X.2017.06.008
Language中文
Citation statistics
Document Type期刊论文
Identifierhttp://ir.giec.ac.cn/handle/344007/16679
Collection中国科学院广州能源研究所
Corresponding Author熊祖鸿
Affiliation1.中国科学院广州能源研究所,广州510640;
2.中国科学院可再生能源重点实验室,广州510640;
3.广东省新能源和可再生能源研究开发与应用重点实验室,广州510640
First Author AffilicationGuangZhou Institute of Energy Conversion,Chinese Academy of Sciences
Recommended Citation
GB/T 7714
鲁敏,熊祖鸿,林霞,等. 外加剂对建筑垃圾再生砖早强性能的影响[J]. 新能源进展,2017,5(6):466-471.
APA 鲁敏,熊祖鸿,林霞,房科靖,郭华芳,&陈勇.(2017).外加剂对建筑垃圾再生砖早强性能的影响.新能源进展,5(6),466-471.
MLA 鲁敏,et al."外加剂对建筑垃圾再生砖早强性能的影响".新能源进展 5.6(2017):466-471.
Files in This Item: Download All
File Name/Size DocType Version Access License
外加剂对建筑垃圾再生砖早强性能的影响.p(1625KB)期刊论文出版稿开放获取CC BY-NC-SAView Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[鲁敏]'s Articles
[熊祖鸿]'s Articles
[林霞]'s Articles
Baidu academic
Similar articles in Baidu academic
[鲁敏]'s Articles
[熊祖鸿]'s Articles
[林霞]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[鲁敏]'s Articles
[熊祖鸿]'s Articles
[林霞]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: 外加剂对建筑垃圾再生砖早强性能的影响.pdf
Format: Adobe PDF
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.