纳米SiO2冻干胶-ATO复合贴膜玻璃的制备及调光隔热性能研究
Alternative TitlePreparation, Light-Dimming and Heat-Insulating Properties of Nano-SiO2 Cryogels-ATO Composite Filmed Glass
周建华1; 刘杰1; 程浩亮1; 苗蕾1; 衣笠直己; 许家友2
2015
Source Publication新能源进展
Issue2Pages:157-162
AbstractNano-silica cryogels and ATO composite dispersion were coated on PET film, and then the coated film was pasted on the glass to prepare filmed glass. The optical and thermal insulation properties of the filmed glass were investigated. The results showed th
Other Abstract将纳米SiO2冻干胶和ATO复合分散液涂覆在PET薄膜上,干燥后贴在玻璃上制成贴膜玻璃,研究了其光学、隔热温差等性能。结果表明,当分散液为10%SiO2+10%ATO时,所得贴膜玻璃具有较好的光谱选择性,可见光透过率为77.2%、近红外屏蔽波长(透过率小于10%)为1500nm、遮蔽系数为0.69;同时贴膜玻璃还具有较好的隔热效果,自制贴膜玻璃试验箱内空气温度比空白玻璃箱内空气温度低8℃。
Keyword调光隔热 Sio2冻干胶 纳米ato 贴膜玻璃
Funding Organization广东省教育部产学研结合项目(20128091000165);广东省高端外国专家项目(GDJ20144400003);中国科学院国际合作局对外合作重点项目(182344KYSB20130006)
Document Type期刊论文
Identifierhttp://ir.giec.ac.cn/handle/344007/16235
Collection中国科学院广州能源研究所
Affiliation1.中国科学院广州能源研究所中国科学院可再生能源重点实验室,广州510640
2.广州大学化学化工学院,广州510006
First Author AffilicationGuangZhou Institute of Energy Conversion,Chinese Academy of Sciences
Recommended Citation
GB/T 7714
周建华,刘杰,程浩亮,等. 纳米SiO2冻干胶-ATO复合贴膜玻璃的制备及调光隔热性能研究[J]. 新能源进展,2015(2):157-162.
APA 周建华,刘杰,程浩亮,苗蕾,衣笠直己,&许家友.(2015).纳米SiO2冻干胶-ATO复合贴膜玻璃的制备及调光隔热性能研究.新能源进展(2),157-162.
MLA 周建华,et al."纳米SiO2冻干胶-ATO复合贴膜玻璃的制备及调光隔热性能研究".新能源进展 .2(2015):157-162.
Files in This Item: Download All
File Name/Size DocType Version Access License
纳米SiO2冻干胶-ATO复合贴膜玻璃的(676KB)期刊论文作者接受稿开放获取CC BY-NC-SAView Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[周建华]'s Articles
[刘杰]'s Articles
[程浩亮]'s Articles
Baidu academic
Similar articles in Baidu academic
[周建华]'s Articles
[刘杰]'s Articles
[程浩亮]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[周建华]'s Articles
[刘杰]'s Articles
[程浩亮]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: 纳米SiO2冻干胶-ATO复合贴膜玻璃的制备及调光隔热性能研究.pdf
Format: Adobe PDF
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.