Catalytic steam reforming of toluene as model tar compound using Ni/coal fly ash catalyst | |
Lu, Min1,2,3; Xiong, Zuhong1,2,3; Li, Jiqing1,2,3; Li, Xi1,2,3; Fang, Kejing1,2,3; Li, Tao1,2,3 | |
2020-06-18 | |
发表期刊 | ASIA-PACIFIC JOURNAL OF CHEMICAL ENGINEERING |
ISSN | 1932-2135 |
页码 | 13 |
通讯作者 | Xiong, Zuhong(xiongzh@ms.giec.ac.cn) |
摘要 | Coal fly ash (CFA), a solid waste from power plants, was selected as the support of Ni-based catalysts used for steam reforming of toluene in a fixed-bed reactor. The CFA support was thermally pretreatment first, followed by chemical activation with different treatment time (6 h to 4 days) in 2-mol/L HNO(3)solution. Then, series low-cost catalysts were prepared by wet impregnation. The prepared catalysts were characterized suitably by X-ray diffraction (XRD), Brunauere-Emmette-Teller (BET), temperature programmed reduction (TPR), temperature programmed desorption (TPD), and Raman techniques. According to the catalyst characterization, the chemical pretreatment could improve the support property by adjusting the chemical composition. The Fe-rich Fe-Ni and Ni-Co alloy was formed by H(2)reduction on the Ni/CFA-6h and Co-Ni/CFA-6h catalysts, respectively. In the catalytic steam reforming of toluene, the Ni/CFA-6h had the best catalytic active among all monometallic catalysts, which could be attributed to the existence of Fe(0.94)Ni(0.06)particles, and its performance could be further improved after partly replacing Ni by Co. The Co-Ni/CFA-6h catalyst exhibited the best ability of carbon deposit resistance, implying that its catalytic performance slightly lower than Ni/SiO(2)was due to the too large S(BET)surface area gap. |
关键词 | carbon deposit catalyst coal fly ash steam reforming toluene |
DOI | 10.1002/apj.2529 |
关键词[WOS] | HYDROGEN-PRODUCTION ; BIOMASS TAR ; NICKEL ; GASIFICATION ; PERFORMANCE ; ALUMINA ; IRON ; COBALT ; SIZE ; CA |
收录类别 | SCI |
语种 | 英语 |
资助项目 | National Natural Science Foundation of China[21606228] |
WOS研究方向 | Engineering |
项目资助者 | National Natural Science Foundation of China |
WOS类目 | Engineering, Chemical |
WOS记录号 | WOS:000540973200001 |
出版者 | WILEY |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.giec.ac.cn/handle/344007/27236 |
专题 | 中国科学院广州能源研究所 |
通讯作者 | Xiong, Zuhong |
作者单位 | 1.Chinese Acad Sci, Guangzhou Inst Energy Convers, Guangzhou 510640, Peoples R China 2.CAS Key Lab Renewable Energy, Guangzhou 510640, Peoples R China 3.Guangdong Prov Key Lab New & Renewable Energy Res, Guangzhou 510640, Peoples R China |
第一作者单位 | 中国科学院广州能源研究所 |
推荐引用方式 GB/T 7714 | Lu, Min,Xiong, Zuhong,Li, Jiqing,et al. Catalytic steam reforming of toluene as model tar compound using Ni/coal fly ash catalyst[J]. ASIA-PACIFIC JOURNAL OF CHEMICAL ENGINEERING,2020:13. |
APA | Lu, Min,Xiong, Zuhong,Li, Jiqing,Li, Xi,Fang, Kejing,&Li, Tao.(2020).Catalytic steam reforming of toluene as model tar compound using Ni/coal fly ash catalyst.ASIA-PACIFIC JOURNAL OF CHEMICAL ENGINEERING,13. |
MLA | Lu, Min,et al."Catalytic steam reforming of toluene as model tar compound using Ni/coal fly ash catalyst".ASIA-PACIFIC JOURNAL OF CHEMICAL ENGINEERING (2020):13. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论