	preparationoftrititanatenanotubeandtemobservation
	Huang C(黄琮)1; Zhang KJ(张开坚)1; Dang Z(党志)1; Li XJ(李新军)2
	2006
发表期刊	journalofinorganicmaterials
ISSN	1000-324X
卷号	21 期号:3 页码:547
摘要	Trititanate nanotubes were synthesized from rutile TiO2 via hydrothermal process. The influences of process parameters such as stirring, acid leaching and calcination temperature on formation and structure of nanotubes were observed by TEM. The results show that continuous stirring could improve the directional growth of TiO2 particles and formation of trititanate nanoflakes, and nanotubes are formed in the acid leaching process. It also reveals that 300 degrees C is the critical transformation temperature between nanotubes and long-stick crystalline column. The nanotubes synthesized under optimal condition are uniform and longer than 1 mu m, and the ratio of length to diameter is 125:1.
语种	英语
文献类型	期刊论文
条目标识符	http://ir.giec.ac.cn/handle/344007/22487
专题	中国科学院广州能源研究所
作者单位	1.华南理工大学 2.中国科学院广州能源研究所
推荐引用方式 GB/T 7714	Huang C,Zhang KJ,Dang Z,et al. preparationoftrititanatenanotubeandtemobservation[J]. journalofinorganicmaterials,2006,21(3):547.
APA	黄琮,张开坚,党志,&李新军.(2006).preparationoftrititanatenanotubeandtemobservation.journalofinorganicmaterials,21(3),547.
MLA	黄琮,et al."preparationoftrititanatenanotubeandtemobservation".journalofinorganicmaterials 21.3(2006):547.