controlonthemorphologyofabaamphiphilictriblockcopolymermicellesindioxanewatermixturesolvent
Gan Yuan; Wang Zhida; Lu Zhuoxin; Shi Yan; Tan Hongyi; Yan Changfeng
2018
发表期刊chinesejournalofpolymerscience
ISSN0256-7679
卷号036期号:006页码:728
摘要This work offers a typical understanding of the factors that govern the nanostructures of poly(4-vinyl pyridine)-b-polystyrene-bpoly(4-vinyl pyridine)(P4 VP-b-PS-b-P4 VP) block copolymers(BCs) in dioxane/water, in which water is a selective solvent for the P4 VP block. It is achieved through an investigation of the amphiphilic triblock copolymer micelles by variation of three different factors, including water content(above CWC but under the immobile concentration), temperature(ranging from 20 °C to 80 °C), and copolymer composition(low and high PS block length). Transition of bead-like micelles to vesicles is observed with the increase of water content due to the increase of interfacial energy between the copolymer and the solvent. Effect of temperature superposed on that of water content results in various morphologies, such as beads, fibers, rods, capsules, toroids, lamellae, and vesicles. The interfacial tension between the BC and the solvent increases with the increase of water content but decreases with the increase of temperature, indicating that the micellar morphologies are resulted from the competitive interplay between the temperature and the water content and always change in a direction that decreases the interfacial energy. Based on the micellar structures obtained in this work and the effects of temperature superposed on water concentration, a diagram of phase evolution of different micellar morphologies is illustrated here, covering the temperature range from 20 °C to 80 °C and the water content changing from 20 vol% to 35 vol%. For the investigation of BC composition, morphological transition of vesicle-to-fiber, for high PS length, is observed as compared with bead-to-capsule for low PS length, as the temperature changes from 20 °C to 80 °C. Our research complements the protocols to control over the morphologies and the phase diagram describing P4 VP-b-PS-b-P4 VP micellar nanostructures in aqueous solution.
语种英语
文献类型期刊论文
条目标识符http://ir.giec.ac.cn/handle/344007/21554
专题中国科学院广州能源研究所
作者单位中国科学院广州能源研究所
第一作者单位中国科学院广州能源研究所
推荐引用方式
GB/T 7714
Gan Yuan,Wang Zhida,Lu Zhuoxin,et al. controlonthemorphologyofabaamphiphilictriblockcopolymermicellesindioxanewatermixturesolvent[J]. chinesejournalofpolymerscience,2018,036(006):728.
APA Gan Yuan,Wang Zhida,Lu Zhuoxin,Shi Yan,Tan Hongyi,&Yan Changfeng.(2018).controlonthemorphologyofabaamphiphilictriblockcopolymermicellesindioxanewatermixturesolvent.chinesejournalofpolymerscience,036(006),728.
MLA Gan Yuan,et al."controlonthemorphologyofabaamphiphilictriblockcopolymermicellesindioxanewatermixturesolvent".chinesejournalofpolymerscience 036.006(2018):728.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Gan Yuan]的文章
[Wang Zhida]的文章
[Lu Zhuoxin]的文章
百度学术
百度学术中相似的文章
[Gan Yuan]的文章
[Wang Zhida]的文章
[Lu Zhuoxin]的文章
必应学术
必应学术中相似的文章
[Gan Yuan]的文章
[Wang Zhida]的文章
[Lu Zhuoxin]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。