	低品位凹凸棒石在E4303电焊条中的应用
其他题名	The Application of Low-grade Palygorskite in E4303 Electrode
	王璨 1,2; 陈雪芳 1,2; 熊莲1,2 ; 张海荣 1,2; 陈新德1,2
	2017-10
发表期刊	广东化工
ISSN	1007-1865
卷号	44 期号:20 页码:35-36
摘要	硫酸改性低品位凹凸棒石显著提高凹凸棒石的含量,然而会造成凹凸棒石中的硫含量大幅提高。而电焊条对药皮中硫含量要求很严格,硫含量高时焊缝容易产生裂纹。为了降低低品位凹凸棒石中的硫含量,本文研究了酸改性低品位凹凸棒石的碱处理工艺,并经过配方研制,成功将低品位凹凸棒石添加到E4303电焊条药皮中,降低了电焊条的生产成本,获得了性能较好的电焊条。
其他摘要	It could significantly improve the attapulgite content of low-grade palygorskite modified by sulfuric acid, however would lead to higher sulfur content of palygorskite noteworthly. The electrode is very strict with sulfur content in the coating, and high sulfur content in electrode welding would crack easily. In order to reduce the sulfur content in the sulfuric acid modified low-grade palygorskite, this paper studies the alkali treatment process of sulfuric acid modified palygorskite. Then, tow-grade palygorskite is added to the E4303 electrode coated successfully after formulation. It would obtain a good welding electrode performance and reduce the cost of production of welding electrode.
关键词	低品位凹凸棒石改性化学组成电焊条 low-gradepalygorskite modification chernical constitution welding electrode
语种	中文
文献类型	期刊论文
条目标识符	http://ir.giec.ac.cn/handle/344007/16554
专题	中国科学院广州能源研究所
通讯作者	陈新德
作者单位	1.中国科学院广州能源研究所，中国科学院可再生能源重点实验室，广东广州510640; 2.中国科学院广州能源所盱眙凹土研发中心，江苏盱眙211700
第一作者单位	中国科学院广州能源研究所
推荐引用方式 GB/T 7714	王璨,陈雪芳,熊莲,等. 低品位凹凸棒石在E4303电焊条中的应用[J]. 广东化工,2017,44(20):35-36.
APA	王璨,陈雪芳,熊莲,张海荣,&陈新德.(2017).低品位凹凸棒石在E4303电焊条中的应用.广东化工,44(20),35-36.
MLA	王璨,et al."低品位凹凸棒石在E4303电焊条中的应用".广东化工 44.20(2017):35-36.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
低品位凹凸棒石在E4303电焊条中的应用（104KB）	期刊论文	出版稿	开放获取	CC BY-NC-SA	浏览下载