Novel core-shell structured Si/S-doped-carbon composite with buffering voids as high performance anode for Li-ion batteries | |
Shao, Dan1,2; Smolianova, Inna1,3; Tang, Daoping1; Zhang, Lingzhi1 | |
2017 | |
发表期刊 | RSC ADVANCES |
ISSN | 2046-2069 |
卷号 | 7期号:5页码:2407-2414 |
摘要 | A novel core-shell structured Si/S-doped-carbon composite with buffering voids (Si/v-SC), was prepared by a facile hydrothermal method using glucose as carbon source and simultaneously chemical polymerization of 3,4-ethylenedioxythiophene (EDOT) in the presence of Si@SiO2 nanoparticles, and followed by carbonization and removal of the SiO2 layer. The results showed that the Si nanoparticles were embedded in the S-doped-carbon buffer space to form a core-shell structure. Compared to the Si/carbon composite (Si/v-C) without S-doping in carbon layer, the Si/v-SC composite electrode showed improved cycling and rate performance, exhibiting a reversible capacity of 664 mA h g(-1) over 300 cycles at the current of 0.4 A g(-1) and a high capacity of 537 mA h g(-1) even at 10 A g(-1). The effects of S-doping on the properties of carbon material were further investigated. XRD and Raman test revealed that the S-doping increased the interspace of carbon crystal face, and improved the amorphous structure of carbon and thus the initial coulombic efficiency. |
文章类型 | Article |
WOS标题词 | Science & Technology ; Physical Sciences |
DOI | 10.1039/c6ra26247c |
研究领域[WOS] | Chemistry |
关键词[WOS] | HIGH-CAPACITY ANODE ; STORAGE PERFORMANCE ; LITHIUM STORAGE ; SILICON ; NANOCOMPOSITES ; NANOSTRUCTURES ; NANOSPHERES ; GRAPHENE ; SULFUR ; SIZE |
收录类别 | SCI |
语种 | 英语 |
项目资助者 | National Natural Science Foundation of China(21573239) ; Guangdong Provincial Project for Science Technology(2014TX 01N014/2014A050503050/2015B010135008) ; Guangzhou Municipal Project for Science Technology(2014Y2-00219/201509010018) ; Wong Education Foundation |
WOS类目 | Chemistry, Multidisciplinary |
WOS记录号 | WOS:000393748600004 |
出版者 | ROYAL SOC CHEMISTRY |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.giec.ac.cn/handle/344007/14030 |
专题 | 中国科学院广州能源研究所 |
通讯作者 | Zhang, Lingzhi |
作者单位 | 1.Chinese Acad Sci, Guangzhou Inst Energy Convers, Key Lab Renewable Energy, Guangzhou 510640, Peoples R China 2.Guangzhou Inst Energy Testing, Guangzhou 510170, Guangdong, Peoples R China 3.Univ Chinese Acad Sci, 19 Yu Quan Rd, Beijing 100049, Peoples R China |
第一作者单位 | 中国科学院广州能源研究所 |
推荐引用方式 GB/T 7714 | Shao, Dan,Smolianova, Inna,Tang, Daoping,et al. Novel core-shell structured Si/S-doped-carbon composite with buffering voids as high performance anode for Li-ion batteries[J]. RSC ADVANCES,2017,7(5):2407-2414. |
APA | Shao, Dan,Smolianova, Inna,Tang, Daoping,&Zhang, Lingzhi.(2017).Novel core-shell structured Si/S-doped-carbon composite with buffering voids as high performance anode for Li-ion batteries.RSC ADVANCES,7(5),2407-2414. |
MLA | Shao, Dan,et al."Novel core-shell structured Si/S-doped-carbon composite with buffering voids as high performance anode for Li-ion batteries".RSC ADVANCES 7.5(2017):2407-2414. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论