Hydrocracking of Polyolefin Thermal Cracking Waxes Over Ni-loaded Molecular Sieve Catalysts | |
Ding, F.1,2; Luo, C.1; Zhang, H.1; Xiong, L.1; Chen, X. D.1 | |
2015 | |
发表期刊 | PETROLEUM SCIENCE AND TECHNOLOGY |
卷号 | 33期号:21-22页码:1846-1852 |
摘要 | The hydrocracking of thermal cracking waxes obtained from pyrolysis of polyolefin at 360 degrees C for 120min has been studied using Ni-loaded molecular sieves catalysts. According to XRD, TPR, and BET data, the presence of nickel oxide did not seem to damage the crystalline framework of the catalytic supports. Hydrocracking experiments were carried out in a stirred autoclave reactor at 300 degrees C for 120min under 2.0 MPa of hydrogen. The results suggested the existence of a balance between the acid and metal function over bifunctional catalysts, which affects hydrogenation and hydroisomerization of thermal cracking waxes. Hydrocracking reactions took place extensively over mixture of Ni/HBeta and ZSM-5, leading toward higher fractions of gases (30.2%) and diesel (23.5%). The higher fractions of gasoline (33.5%) and lube base oil (19.0%) were obtained over mixture of Ni/HSAPO-11 and ZSM-5. In contrast, hydrocracking reaction occurred in a lower extent over mixture of Ni/NMCM-41 and ZSM-5, which produces lube base oil with lower pour point (-10 degrees C), gasoline and diesel with lower bromine numbers (1.1 and 0.8g Br-2/100g sample). The viscosity index of lube base oil was in the range of 131-171 over all three mixed catalysts. |
文章类型 | Article |
关键词 | Hydrocracking Hydrogenation Hydroisomerization Polyolefin Thermal Cracking Waxes |
WOS标题词 | Science & Technology ; Technology |
DOI | 10.1080/10916466.2012.671401 |
研究领域[WOS] | Energy & Fuels ; Engineering |
关键词[WOS] | OIL ; HYDROISOMERIZATION ; POLYETHYLENE ; ZEOLITE |
收录类别 | SCI |
语种 | 英语 |
WOS类目 | Energy & Fuels ; Engineering, Chemical ; Engineering, Petroleum |
WOS记录号 | WOS:000367155200010 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.giec.ac.cn/handle/344007/10933 |
专题 | 中国科学院广州能源研究所 |
作者单位 | 1.Chinese Acad Sci, Key Lab Renewable Energy & Gas Hydrate, Guangzhou, Guangdong, Peoples R China 2.Grad Univ Chinese Acad Sci, Beijing, Peoples R China |
推荐引用方式 GB/T 7714 | Ding, F.,Luo, C.,Zhang, H.,et al. Hydrocracking of Polyolefin Thermal Cracking Waxes Over Ni-loaded Molecular Sieve Catalysts[J]. PETROLEUM SCIENCE AND TECHNOLOGY,2015,33(21-22):1846-1852. |
APA | Ding, F.,Luo, C.,Zhang, H.,Xiong, L.,&Chen, X. D..(2015).Hydrocracking of Polyolefin Thermal Cracking Waxes Over Ni-loaded Molecular Sieve Catalysts.PETROLEUM SCIENCE AND TECHNOLOGY,33(21-22),1846-1852. |
MLA | Ding, F.,et al."Hydrocracking of Polyolefin Thermal Cracking Waxes Over Ni-loaded Molecular Sieve Catalysts".PETROLEUM SCIENCE AND TECHNOLOGY 33.21-22(2015):1846-1852. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论