Single-walled carbon nanotubes prepared in small AlPO4-5 and CoAPO-5 molecular sieves by low-temperature hydrocracking | |
Yang, Wenshen1; Sun, Weina1,2; Zhao, Shuheng1,2; Yin, Xiuli1 | |
2016 | |
发表期刊 | MICROPOROUS AND MESOPOROUS MATERIALS |
卷号 | 219页码:87-92 |
摘要 | Single-walled carbon nanotubes (SWNTs) were prepared in the channels of small AlPO4-5 and cobalt-incorporated AlPO4-5 (CoAPO-5) crystals (4-6 mu m in diameter and 10-30 mu m in length), by hydrocracking at 350 degrees C. The effects of Co content in the precursor gel and carbon density of the structure-directing agent on the resulting SWNTs were investigated. The results of high-resolution transmission electron microscopy and polarized Raman scattering indicated that SWNTs formed in the channels of AlPO4-5 and CoAPO-5 crystals, after hydrocracking for 10 h at 350 degrees C. The SWNTs were 0.4 nm in diameter, and possessed well-defined symmetry. When the Co/Al ratio of the precursor gel was 0.075, the relative intensity ratio of Raman D to G band (ID/IG) was 0.286, and the weight loss (500-700 C) of the SWNTs formed in CoAPo-5 was 3.27 wt%. This Co/Al ratio yielded the lowest obtained I-D/I-G value and the highest weight loss of SWNTs, which indicated the lowest amorphous carbon density and the highest SWNT quantity. The density and quantity of SWNTs in the AlPO4-5 crystals increased when the structure-directing agent was changed from triethylamine to tripropylamine, because of the higher carbon content of the latter's unit cell. Low-temperature hydrocracking can be used to prepare SWNTs in the channels of AlPO4-5 and CoAPO-5 crystals, even for small low-quality crystals. (C) 2015 Elsevier Inc. All rights reserved. |
文章类型 | Article |
关键词 | Single-walled Carbon Nanotubes Hydrocracking Coapo-5 Crystals Radial Breathing Mode Co/al Ratio |
WOS标题词 | Science & Technology ; Physical Sciences ; Technology |
DOI | 10.1016/j.micromeso.2015.06.036 |
研究领域[WOS] | Chemistry ; Science & Technology - Other Topics ; Materials Science |
关键词[WOS] | CHANNELS ; CRYSTALS ; GROWTH ; DECOMPOSITION ; MECHANISM ; TEMPLATE |
收录类别 | SCI |
语种 | 英语 |
WOS类目 | Chemistry, Applied ; Chemistry, Physical ; Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary |
WOS记录号 | WOS:000363353800012 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.giec.ac.cn/handle/344007/10880 |
专题 | 中国科学院广州能源研究所 |
作者单位 | 1.Chinese Acad Sci, Guangzhou Inst Energy Convers, CAS Key Lab Renewable Energy, Guangzhou 510640, Guangdong, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
第一作者单位 | 中国科学院广州能源研究所 |
推荐引用方式 GB/T 7714 | Yang, Wenshen,Sun, Weina,Zhao, Shuheng,et al. Single-walled carbon nanotubes prepared in small AlPO4-5 and CoAPO-5 molecular sieves by low-temperature hydrocracking[J]. MICROPOROUS AND MESOPOROUS MATERIALS,2016,219:87-92. |
APA | Yang, Wenshen,Sun, Weina,Zhao, Shuheng,&Yin, Xiuli.(2016).Single-walled carbon nanotubes prepared in small AlPO4-5 and CoAPO-5 molecular sieves by low-temperature hydrocracking.MICROPOROUS AND MESOPOROUS MATERIALS,219,87-92. |
MLA | Yang, Wenshen,et al."Single-walled carbon nanotubes prepared in small AlPO4-5 and CoAPO-5 molecular sieves by low-temperature hydrocracking".MICROPOROUS AND MESOPOROUS MATERIALS 219(2016):87-92. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论