Characterization of anorthite-based porcelain prepared by using wollastonite as a calcium source | |
Wang, Shumei1; Qi, Xiaoling2; Hu, Jilin1; Tian, Xiuying1 | |
2015-06-01 | |
发表期刊 | JOURNAL OF CERAMIC PROCESSING RESEARCH |
卷号 | 16期号:3页码:361-365 |
摘要 | The porcelain based on anorthite (CaO center dot Al2O3 center dot 2SiO(2)) has been developed using wollastonite (CaO center dot SiO2) as a calcium source. The slip casting was applied to obtain green body with high-strength. The sintering behaviors of the green specimens were evaluated by determining linear shrinkage, water absorption, bulk density and flexural strength. It was found that the anorthite porcelain fired at 1215 degrees C had excellent technical properties such as water absorption: 0.00% and flexural strength: 109.5 MPa. X-ray diffraction (XRD) and scanning electron microscopy (SEM) analysis results showed the high flexural strength was due to the densification of microstructures and the formation of high crystalline content in the porcelain body. In addition, thermal expansion performance and appearance quality of the final product were discussed. |
文章类型 | Article |
关键词 | Anorthite Porcelain Wollastonite Calcium Source |
WOS标题词 | Science & Technology ; Technology |
研究领域[WOS] | Materials Science |
关键词[WOS] | BONE CHINA ; FIRING TEMPERATURE ; PREFIRED MATERIALS ; BENDING STRENGTH ; RAW-MATERIALS ; LOW-CLAY ; CERAMICS ; MICROSTRUCTURE ; FABRICATION ; ALUMINA |
收录类别 | SCI |
语种 | 英语 |
WOS类目 | Materials Science, Ceramics |
WOS记录号 | WOS:000360832100016 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.giec.ac.cn/handle/344007/10857 |
专题 | 中国科学院广州能源研究所 |
作者单位 | 1.Hunan Inst Humanities Sci & Technol, Loudi 417001, Peoples R China 2.Chinese Acad Sci, Guangzhou Inst Energy Convers, Energy Strategy Res Ctr, Guangzhou 510540, Guangdong, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Shumei,Qi, Xiaoling,Hu, Jilin,et al. Characterization of anorthite-based porcelain prepared by using wollastonite as a calcium source[J]. JOURNAL OF CERAMIC PROCESSING RESEARCH,2015,16(3):361-365. |
APA | Wang, Shumei,Qi, Xiaoling,Hu, Jilin,&Tian, Xiuying.(2015).Characterization of anorthite-based porcelain prepared by using wollastonite as a calcium source.JOURNAL OF CERAMIC PROCESSING RESEARCH,16(3),361-365. |
MLA | Wang, Shumei,et al."Characterization of anorthite-based porcelain prepared by using wollastonite as a calcium source".JOURNAL OF CERAMIC PROCESSING RESEARCH 16.3(2015):361-365. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论