Nano-MoS2/poly (3,4-ethylenedioxythiophene): Poly(styrenesulfonate) composite prepared by a facial dip-coating process for Li-ion battery anode | |
Zhao, Xueling1,2; Mai, Yongjin1; Luo, Hao1; Tang, Daoping1; Lee, Binghui; Huang, Chungui; Zhang, Lingzhi1 | |
2014 | |
发表期刊 | APPLIED SURFACE SCIENCE |
卷号 | 288页码:736-741 |
摘要 | MoS2/poly (3,4-ethylenedioxythiophene): poly(styrenesulfonate) (PEDOT: PSS) composite (MoS2/P) was prepared through a facial and environmental friendly dip-coating method by dispersing nanostructured MoS2 particles in PEDOT: PSS aqueous solution and subsequent filtering process. The characterization of XRD, FTIR, TGA, SEM and TEM revealed that the surface of rose-like MoS2 was homogeneously coated with a thin layer of PEDOT: PSS. After coating, MoS2/P composite showed an enhanced electric conductivity of 1.0 x 10(-1) S/cm, about 5 times of that (2.2 x 10(-2) S/cm) of the pristine MoS2. MoS2/P composite electrode exhibited significantly improved electrochemical performances such as cyclability and rate capability. Half-cell tests showed that MoS2/P composite electrode delivered a reversible capacity of 712 mAh g(-1) at a current density of 50 mA g(-1) and retained 81% capacity after 100 cycles. At a higher current density of 200/300 mA g(-1), it still retained a capacity of 439/363 mAh g(-1) respectively, as compared to 191/140 mAh g(-1) for the pristine MoS2. (C) 2013 Elsevier B. V. All rights reserved. |
文章类型 | Article |
关键词 | Mos2 Anode Poly (3 4-ethylenedioxythiophene): Poly(Styrenesulfonate) |
WOS标题词 | Science & Technology ; Physical Sciences ; Technology |
DOI | 10.1016/j.apsusc.2013.10.142 |
研究领域[WOS] | Chemistry ; Materials Science ; Physics |
关键词[WOS] | LITHIUM STORAGE PROPERTIES ; CATHODE MATERIALS ; ELECTROCHEMICAL CHARACTERIZATION ; MOLYBDENUM-DISULFIDE ; GRAPHITE-ELECTRODES ; ASSISTED SYNTHESIS ; CARBON NANOTUBES ; MOS2 ; NANOCOMPOSITE ; INTERCALATION |
收录类别 | SCI |
语种 | 英语 |
WOS类目 | Chemistry, Physical ; Materials Science, Coatings & Films ; Physics, Applied ; Physics, Condensed Matter |
WOS记录号 | WOS:000327493400101 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.giec.ac.cn/handle/344007/10707 |
专题 | 中国科学院广州能源研究所 |
作者单位 | 1.Chinese Acad Sci, Guangzhou Inst Energy Convers, Guangzhou 510640, Guangdong, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
第一作者单位 | 中国科学院广州能源研究所 |
推荐引用方式 GB/T 7714 | Zhao, Xueling,Mai, Yongjin,Luo, Hao,et al. Nano-MoS2/poly (3,4-ethylenedioxythiophene): Poly(styrenesulfonate) composite prepared by a facial dip-coating process for Li-ion battery anode[J]. APPLIED SURFACE SCIENCE,2014,288:736-741. |
APA | Zhao, Xueling.,Mai, Yongjin.,Luo, Hao.,Tang, Daoping.,Lee, Binghui.,...&Zhang, Lingzhi.(2014).Nano-MoS2/poly (3,4-ethylenedioxythiophene): Poly(styrenesulfonate) composite prepared by a facial dip-coating process for Li-ion battery anode.APPLIED SURFACE SCIENCE,288,736-741. |
MLA | Zhao, Xueling,et al."Nano-MoS2/poly (3,4-ethylenedioxythiophene): Poly(styrenesulfonate) composite prepared by a facial dip-coating process for Li-ion battery anode".APPLIED SURFACE SCIENCE 288(2014):736-741. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论