Highly activated Ag-doped Fe-based catalysts designed for Fischer-Tropsch synthesis
Zhang, Yulan1,2; Ma, Longlong1; Wang, Tiejun1; Li, Xinjun1
2015
发表期刊RSC ADVANCES
卷号5期号:56页码:45426-45430
摘要Ag-doped Fe-based microspheres were synthesized via a one-pot solvothermal method, and displayed excellent mechanical stability and catalytic activity. Especially, the catalyst at Ag/Fe = 1 showed the lowest selectivity to CH4 (12.6 wt%) and the highest to C2-4 olefins (29.0 wt%), as well as a good selectivity to gasoline-range (C5-11) fraction products (45.7 wt%). In addition, the catalytic activity and product selectivity of Ag/Fe measured at 280 degrees C was superior to that at 270 degrees C and 260 degrees C.
文章类型Article
WOS标题词Science & Technology ; Physical Sciences
DOI10.1039/c5ra08444j
研究领域[WOS]Chemistry
关键词[WOS]CO/SBA-15 CATALYSTS ; MONODISPERSE ; HOLLOW
收录类别SCI
语种英语
WOS类目Chemistry, Multidisciplinary
WOS记录号WOS:000354965300080
引用统计
被引频次:6[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.giec.ac.cn/handle/344007/10503
专题中国科学院广州能源研究所
作者单位1.Chinese Acad Sci, Guangzhou Inst Energy Convers, Key Lab Renewable Energy, Guangzhou 510640, Guangdong, Peoples R China
2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China
第一作者单位中国科学院广州能源研究所
推荐引用方式
GB/T 7714
Zhang, Yulan,Ma, Longlong,Wang, Tiejun,et al. Highly activated Ag-doped Fe-based catalysts designed for Fischer-Tropsch synthesis[J]. RSC ADVANCES,2015,5(56):45426-45430.
APA Zhang, Yulan,Ma, Longlong,Wang, Tiejun,&Li, Xinjun.(2015).Highly activated Ag-doped Fe-based catalysts designed for Fischer-Tropsch synthesis.RSC ADVANCES,5(56),45426-45430.
MLA Zhang, Yulan,et al."Highly activated Ag-doped Fe-based catalysts designed for Fischer-Tropsch synthesis".RSC ADVANCES 5.56(2015):45426-45430.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zhang, Yulan]的文章
[Ma, Longlong]的文章
[Wang, Tiejun]的文章
百度学术
百度学术中相似的文章
[Zhang, Yulan]的文章
[Ma, Longlong]的文章
[Wang, Tiejun]的文章
必应学术
必应学术中相似的文章
[Zhang, Yulan]的文章
[Ma, Longlong]的文章
[Wang, Tiejun]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。